Stämpel/Etikett Security stamp/lable BLÄSTRING BLASTING Granskad av Reviewed by Villy Johansson Tjst Dept. KEG This document and its contents is the property of BAE Systems Bofors AB and must not be reproduced, disclosed to any third party or used in any unauthorized manner without written consent. tb_tvåspråkig 2006-05-09 1 (16)
ÄNDRINGSFÖRTECKNING RECORD OF CHANGES Ändring nummer Revision No. ÄB-nr Rev. requision No. Äo-nr Rev order No. 1 02853614 39084838 Berörda paragrafer + kort beskrivning Relevant paragraph + brief description Punkt 1, 2, 5, 5.2, 6.1, 6.3.1 och 7.2: text uppdaterad. Punkt 5, 6 och 8.4 i utgåva 01 utgår. 2 02873074 Tekniska förändringar: Pkt. 2 Referens till iso 8503-2 tillagd. 39088761 Pkt. 6.3.2 Textstycke uppdaterat m.a.p. lätt-blästring Pkt. 6.3.3 Textstycke uppdaterat m.a.p. ytprofilklass Pkt. 7.1 Textstycke kompletterat m.a.p. svetsfogar. Pkt. 7.1 Sista kontrollkriteriet kompletterat med ytprofilklass Tabell 1. Referens till glaskuleblästring borttaget från ritningskod BL02 3 39093849 Kod BL03 tillkom (våtblästring). Redaktionella förändringar: Pkt. 6.3.1 6.3.5 Byte av namn på rubriker Pkt. 6.3.1 ändrad referens till pkt. 7 4 39094119 Hänvisning till TB 00816967 borttagen. tb_tvåspråkig 2006-05-09 2 (16)
Innehållsförteckning 1 Omfattning... 4 2 Referenser... 4 3 Ritningskoder... 4 4 Allmänna krav... 4 5 Material... 5 5.1 Allmänt... 5 5.2 Krav på blästermedel... 5 5.3 Krav på maskeringsmaterial... 5 6 Utförande... 5 6.1 Allmänt... 5 6.2 Utförande före blästring... 7 6.2.1 Allmänt... 7 6.2.2 Rengöring... 7 6.2.3 Maskering... 7 6.3 Blästring... 7 6.3.1 Allmänt... 7 6.3.2 Blästring som rengöring och aktivering... 7 6.3.3 Blästring som förbehandling före målning... 8 6.3.4 Blästring som förbehandling för termisk sprutning... 8 6.3.5 Blästring för avlägsnande av ytbehandlingsskikt... 8 7 Kontroll... 8 7.1 Artikelkontroll... 8 Bilder och tabeller... 15 tb_tvåspråkig 2006-05-09 3 (16)
1 Omfattning Denna bestämmelse fastställer de krav som BAE Systems Bofors AB (Bofors) ställer vid blästring av metalliska material med följande syfte: - Rengöring och aktivering. - Förbehandling före målning och termisk sprutning. - Avlägsnande av ytbehandlingsskikt. Om inte annat anges gäller generella krav enligt teknisk bestämmelse (TB). 2 Referenser Följande dokument utgör, i tillämplig omfattning, en del av denna bestämmelse. Såvida inte en särskild utgåva anges, avses den senaste utgåvan. SS-EN ISO 8501-1 Behandling av stålytor före beläggning med målningsfärg och liknande produkter - Visuell utvärdering av ytrenhet. Del 1: Rostgrader och förbehandlingsgrader för obelagt stål och för stål, från vars hela yta tidigare beläggning avlägsnats SS-ISO 8503-2 Behandling av stålytor före beläggning med målningsfärg och liknande produkter - Karakterisering av ytråhet hos blästrade stålunderlag - Del 2: Metod för klassning av ytprofil hos blästrat stål - Komparatormetod SS-EN ISO 8504-2 Behandling av stålytor före beläggning med målningsfärg och liknande produkter - Förbehandlingsmetoder - Del 2: Blästring 3 Ritningskoder Tabell 1 anger ritningskoder för olika typer av blästring. 4 Allmänna krav Om fordringarna på blästring avviker från reglerna i denna standard ska avvikelsen anges på konstruktionsunderlaget. Tätningsytor för O-ringar, lagerytor, polerade ytor och andra ytor där blästring kan vara skadlig för konstruktionen, ska maskeras före blästring. Maskering av ytorna ska anges på konstruktionsunderlaget. tb_tvåspråkig 2006-05-09 4 (16)
5 Material 5.1 Allmänt Material och processer ska väljas så att kraven i pkt 5 innehålls. 5.2 Krav på blästermedel Blästermedelstyp och kornstorlek ska baseras på krav såsom renhet och ytprofil. Blästermedel och eventuella blästermedelsrester får ej orsaka galvanisk korrosion på den blästrade ytan. Riktlinjer för val av blästermedel ges i tabell 2. 5.3 Krav på maskeringsmaterial Maskeringsmaterial ska: - vara fritt från silikoner - ej överföra adhesiv till artikelns yta - längs maskeringens kanter ej uppvisa tecken på penetration eller resning vid blästring med 90 anslagsvinkel vid specificerat munstyckstryck. 6 Utförande 6.1 Allmänt Ytor som enligt konstruktionsunderlaget inte ska blästras ska maskeras enligt pkt 6.2.3. Blästring ska vanligtvis ej utföras förrän efter avslutande av följande operationer: Plastisk bearbetning såsom bockning, riktning, sträckformning, sträckriktning etc. Avgradning och fasning av kanter, hörn, hål etc. Värmebehandling. Oförstörande provning. tb_tvåspråkig 2006-05-09 5 (16)
Hårdlödning, punktsvetsning och maskinell smältsvetsning. tb_tvåspråkig 2006-05-09 6 (16)
6.2 Utförande före blästring 6.2.1 Allmänt Ytavvikelser såsom repor, grov korrosion, grader, vassa kanter, svetssprut eller slagg ska avlägsnas från ytan. 6.2.2 Rengöring Om ytan är förorenad med olja eller fett ska avfettning utföras. Om en visuell standard eller likare är specificerad som komplement ska ytans tillstånd bestämmas innan blästring påbörjas. 6.2.3 Maskering Ytor som inte ska blästras ska maskeras med tejp och toleranssatta hål ska pluggas igen. Såvida inte annat anges i tillverkningsunderlaget ska följande kriterier uppfyllas: toleransen för blästringens utbredning ska vara 0 till +3 mm för hål med diameter 12 mm är blästring valfri faser vid hål ska inte maskeras gängor och splines maskeras O-ringsspår maskeras. 6.3 Blästring 6.3.1 Allmänt För varje materialtyp ska typ av blästermedel samt blästerparametrar, såsom munstyckstryck, anslagsvinkel och arbetsavstånd, väljas så att kraven i punkt 7 uppfylls. 6.3.2 Blästring som rengöring och aktivering Med syfte att rengöra och aktivera ytan kan blästring användas som alternativ till kemiska metoder. tb_tvåspråkig 2006-05-09 7 (16)
Om inte annat anges gäller generella krav enligt denna tekniska bestämmelse. För denna typ av blästring finns ingen specifik ritningskod. Målade komponenter och halvfabrikat med ett väl vidhäftande färgskikt, lämpligt som underlag för täckmålning, kan matteras genom lätt blästring. Blästermedel och blästerparametrar ska väljas så att målningsskiktet i huvudsak bibehålls intakt. 6.3.3 Blästring som förbehandling före målning Blästring ska utföras till förbehandlingsgrad och ytprofilklass motsvarande specificerad visuell standard eller likare. Om inte annat anges ska ytan blästras till förbehandlingsgrad motsvarande min Sa 2 ½ enligt SS-EN ISO 8501-1 samt ytprofilklass fin eller medium enligt SS-ISO 8503-2. 6.3.4 Blästring som förbehandling för termisk sprutning Vid blästring före termisk sprutning ska om inte annat anges: blästerparameterar och blästermedel väljas så att en ytprofil motsvarande Ra~10 µm erhålls ytan blästras till förbehandlingsgrad motsvarande min Sa 3 enligt SS-EN ISO 8501-1. 6.3.5 Blästring för avlägsnande av ytbehandlingsskikt Blästring för avlägsnande av ytbehandlingsskikt används exempelvis som åtgärd vid tillverkningsfel. Ytan ska efter blästring uppfylla de ursprungliga kraven. För denna typ av blästring finns ingen specifik ritningskod. 7 Kontroll 7.1 Artikelkontroll Samtliga artiklar ska efter rengöring kontrolleras med avseende på utseende. Artiklarna ska: tb_tvåspråkig 2006-05-09 8 (16)
ha ett homogent utseende. vara fria från blästermedelsrester, damm och lösa partiklar. vara fria från synliga föroreningar av olja, fett eller andra föroreningar. innehålla ritningskravet avseende dimension och ytfinhet. motsvara förbehandlingsgrad och ytprofilklass hos visuell standard eller likare om sådan specificerats. Svetsfogar ska vara helt fria från slagg och oxider. tb_tvåspråkig 2006-05-09 9 (16)
Table of contents 1 Scope... 11 2 References... 11 3 Drawing codes... 11 4 General requirements... 11 5 Materials... 12 5.1 General... 12 5.2 Requirements on blasting media... 12 5.3 Requirements on masking material... 12 6 Procedures... 12 6.1 General... 12 6.2 Procedures prior to blasting... 13 6.2.1 General... 13 6.2.2 Cleaning... 13 6.2.3 Masking... 13 6.3 Blasting... 14 6.3.1 General... 14 6.3.2 Blasting as cleaning and refreshing... 14 6.3.3 Blasting as pre-treatment prior to painting... 14 6.3.4 Blasting as pre-treatment prior to thermal spraying... 14 6.3.5 Blasting for removal of surface treatment... 15 7 Inspection... 15 7.1 Part inspection... 15 Objects and tables... 15 tb_tvåspråkig 2006-05-09 10 (16)
1 Scope This specification establishes the BAE Systems Bofors AB (Bofors) requirements at abrasive blasting of metallic materials with the following purposes: - Cleaning and refreshing. - Pre-treatment prior to painting and thermal spraying. - Removal of surface treatment. Unless otherwise stated, general requirements according to technical specification (TS). 2 References The following documents shall be considered a part of this specification to the extent indicated. Except where a specific issue is stated, the current issue applies. ISO 8501-1 ISO 8503-2 ISO 8504-2 Preparation of steel substrates before application of paints and related products - Visual assessment of surface cleanliness Part 1: Rust grades and preparation grades of uncoated steel substrates and of steel substrates after overall removal of previous coatings Preparation of steel substrates before application of paints and related products -- Surface roughness characteristics of blastcleaned steel substrates -- Part 2: Method for the grading of surface profile of abrasive blast-cleaned steel -- Comparator pro Preparation of steel substrates before application of paints and related products -- Surface preparation methods -- Part 2: Abrasive blast-cleaning 3 Drawing codes Table 1 states drawing codes for different types of blasting. 4 General requirements If the requirements for blasting deviate from this standard, the deviation shall be specified on the design document. tb_tvåspråkig 2006-05-09 11 (16)
Faces of sealing joints for O-rings, bearing surfaces, polished surfaces and other surfaces where blasting may be detrimental for the design, shall be masked prior to blasting. Masking of the surfaces shall be stated on the design document. 5 Materials 5.1 General Materials and processes shall be chosen to fulfil the requirements in para. 5. 5.2 Requirements on blasting media The selection of abrasive size and type shall be based on the requirements such as cleanliness and roughness. The blasting media and possible blasting media residues shall not cause galvanic corrosion on the blasted surface. Guidelines for selection of blasting media are given in table 2. 5.3 Requirements on masking material The masking material shall: - be free from silicones - not transfer adhesive to the part surface - show no signs of penetration or lifting at the edges of the masking when blasting at 90 angle of incidence at specified nozzle pressure. - 6 Procedures 6.1 General Areas not to be blasted, according to the design document, shall be masked per para 6.2.3. Blasting shall not normally be applied to parts until the completion of the following operations: Forming, involving bending, drawing, stretch forming, stretch straightening etc. tb_tvåspråkig 2006-05-09 12 (16)
Deburring and chamfering of edges, corners, holes etc. Heat treatment Non-destructive testing. Brazing, spot welding and mechanical fusion welding. 6.2 Procedures prior to blasting 6.2.1 General Surface imperfections such as scratches, severe corrosion, sharp fins, sharp edges, weld spatter or burning slag should be removed from the surface. 6.2.2 Cleaning If the surface is contaminated with deposits of oil or grease it shall be cleaned. If a visual standard or comparator is specified as a complement, the condition of the surface prior to blasting should be determined before the blasting commences. 6.2.3 Masking Mask areas not to be blasted using adhesive tape and plug toleranced holes. Unless otherwise specified in the manufacturing documents, the following criteria shall be met: the tolerance for the extension of blasting shall be from 0 to +3 mm for holes with a diameter 12 mm blasting is optional chamfers near holes shall not be masked threads and splines shall be masked O-ring grooves shall be masked. tb_tvåspråkig 2006-05-09 13 (16)
6.3 Blasting 6.3.1 General For each type of material, type of blasting media and blasting parameters, such as nozzle pressure, angle of incidence and working distance, shall be chosen to meet the requirements in para 7. 6.3.2 Blasting as cleaning and refreshing With the purpose of cleaning and refreshing a surface, blasting may be used as an alternative to chemical methods. Unless otherwise stated, general requirements according to this technical specification are valid. No specific drawing code exists for this type of blasting. Painted components and semi-finished products with a well adherent coating suitable as a base for application of top coat, may be refreshed using light blasting. Blasting media and blasting parameters shall be chosen so the coating is principally intact. 6.3.3 Blasting as pre-treatment prior to painting Blasting shall be performed to a surface condition and surface-profile matching specified visual standards or comparators. Unless otherwise specified, the surface shall be blasted to preparation grade corresponding to min Sa 2 ½ according to ISO 8501-1 and surface-profile class fine or medium in accordance with SS-ISO 8503-2. 6.3.4 Blasting as pre-treatment prior to thermal spraying When blasting prior to thermal spraying shall, unless otherwise specified: blasting parameters and blasting media be selected so the resulting surface roughness corresponds to Ra ~10 µm the surface be blasted to a preparation grade corresponding to min Sa 3 according to ISO 8501-1. tb_tvåspråkig 2006-05-09 14 (16)
6.3.5 Blasting for removal of surface treatment Blasting for removal of surface treatment is for instance used as a corrective measure. The surface shall meet the original requirements after blasting. No specific drawing code exists for this type of blasting. 7 Inspection 7.1 Part inspection All parts shall be inspected regarding the appearance after cleaning. The parts shall: be of uniform appearance. be free from residual grit, dust and loose residues. be free from visible deposits of oil, grease or other contaminants. meet the drawing requirements for dimensions and surface finish. correspond to a preparation grade and surface-profile class matching a visual standard or comparator, if specified Welded joints shall be completely free of slag and oxides. tb_tvåspråkig 2006-05-09 15 (16)
BILDER OCH TABELLER / OBJECTS AND TABLES Tabell 1 / Table 1: Ritningskoder / Drawing codes Kod Code Typ av blästring Type of blasting Applikation Application Tidigare beteckning Older designation BL01 Förbehandling (torrblästring) Pre-treatment Före målning Prior to painting Sa1,Sa2,Sa2.5,Sa3 BL02 Förbehandling (glaskulebl.) Pre-treatment Före målning Prior to painting Sa1,Sa2,Sa2.5,Sa3 BL03 Förbehandling (våtblästring) Pre-treatment Före målning Prior to painting Sa1,Sa2,Sa2.5,Sa3 Tabell 2 / Table 2: Riktlinjer för val av blästermedel / Guidelines for selection of blasting media Material Aluminium Stål Steel Rosthärdiga stål Corrosion resistant steel Titan Titanium Nickellegeringar Nickel alloys Allmänt General Applikation/ Application Allmän användning General applications Före målning / Prior to painting Mekanisk rengöring (färdigbearbetad yta) Mechanical cleaning (finished surfaces) Allmän användning General applications Mekanisk rengöring (färdigbearbetad yta) Mechanical cleaning (finished surfaces) Toleranssatta ytor Toleranced areas Blästermedel Blasting media Aluminiumoxid 1) Alumina 1) Enligt ISO 8504-2 According to ISO 8504-2 Aluminiumoxid 2) Alumina 2) Aluminiumoxid Alumina Aluminiumoxid 2) Alumina 2) Glaskulor Glass beads 1) Andra ickemetalliska blästermedel får användas, dock ej kiselkarbid. Other non-metallic media may be used, except silicon carbide. 2) Vid blästring av icke färdigbearbetad yta får andra blästermedel användas. Blasting of surfaces which are not mill finished may be carried out using other blasting media. tb_tvåspråkig 2006-05-09 16 (16)